Assessing push-out bond strength in re-irradiated teeth: Universal resin cement performance in self-etch and self-adhesive modes.

OBJECTIVES: To investigate the effect of cumulative doses of radiation on the pushout bond strength (BS) of a universal resin cement used in the self-etch (SE) and self-adhesive (SA) modes to the intraradicular dentin. MATERIALS AND METHODS: Forty-eight human teeth were distributed into three groups (n = 16) according to the radiation therapy dose (RT): NoRT (no-radiotherapy), 70RT (70 Gy), and 70 + 70RT (70 Gy + 70 Gy). The teeth were redistributed into two subgroups (n = 8), according to the adhesive mode: SE (NoRT-SE, 70RT-SE, and 70 + 70RT-SE) and SA (NoRT-SA, 70RT-SA, and 70 + 70RT-SA). Data were statistically compared after BS test (ANOVA, Tukey's post hoc test, and Fisher's exact test). RESULTS: In the SA mode, BS was significantly higher in nonirradiated teeth compared with 70RT and 70 + 70RT (p < 0.0001). There were no significant differences between SE and SA modes in nonirradiated teeth (p = 0.14). In the 70RT group, SE mode increased BS compared with SA mode (p < 0.0001). Most specimens had adhesive and mixed failures in SA and SE modes, respectively. CONCLUSIONS: The universal resin cement in the SE mode had greater BS to the irradiated dentin. When teeth were re-irradiated, the universal resin cement had similar performance in terms of BS, regardless of the adhesive approach. CLINICAL SIGNIFICANCE: There is no research establishing a correlation between radiotherapy and its impact on the BS of a universal resin cement used in SE and SA modes to intraradicular dentin.

Effect of phosphoric acid containing polyvinylpyrrolidone as protective etchant for dentin bonding.

STATEMENT OF PROBLEM: Phosphoric acid is commonly used in dentistry as an etchant but can result in excessive demineralization of dentin, a major contributor to the instability of dentin-bonded restorations. Nevertheless, research on the development of etchants that can reduce acid damage is sparse. PURPOSE: The purpose of this in vitro study was to investigate the effects of polyvinylpyrrolidone-modified phosphoric acid on the dentin bonding of an etch-and-rinse adhesive. MATERIAL AND METHODS: Protective etchants were prepared by adding polyvinylpyrrolidone to 35% phosphoric acid aqueous solutions: the 3 concentrations were 0.5% (P0.5% group), 1% (P1% group), and 2% (P2% group) w/v. The treatment agent of the control group (C) was 35% phosphoric acid gel. Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), microhardness, microtensile bonding strength (µTBS), nanoleakage, and in situ zymography were used to evaluate the appearance of the protective etchant on dentin bonding. The results were analyzed with a 1-way ANOVA test (α=.05). RESULTS: SEM showed no obviously exposed collagen fiber in the P1% and P2% groups. FTIR showed less demineralization of the dentin surface, and microhardness was higher after treatment with the protective etchant (P<.05). The µTBS of P1% (70 ±9.2 MPa) was the highest, and group C (44 ±5.8 MPa) was the lowest in all groups (P<.05). Moreover, there was weaker MMP activity in the P1% and P2% groups (P<.05). CONCLUSIONS: This study demonstrated that the protective etchant effectively reduced demineralization, enhanced bond strength, and reduced nanoleakage and enzyme activity within the hybrid layer.

Polyvinylpyrrolidone as a primer for resin-dentin bonding.

OBJECTIVE: This study aimed to investigate the effects of polyvinylpyrrolidone (PVP)-containing primer (PCP) on dentin bonding. METHODS: PVP and anhydrous ethanol were used to prepare the PCPs, which were prepared at concentrations of 0.5%, 1%, and 2% (w/v). These PCPs were subsequently applied to the dentin surface, denoted as E1, E2, and E3, respectively. In the control group, no primer was applied. Following the treatment, the dentin surfaces were subjected to analysis using Fourier-transform infrared spectroscopy (FTIR), and the micro-tensile bond strength (MTBS) was evaluated. The failure mode, nanoleakage, and bonding longitudinal section were observed utilizing scanning electron microscopy (SEM). Additionally, the effect of PCPs on matrix metalloproteinases (MMPs) activity was analyzed through an in situ zymography test. Data were subjected to statistical analysis using ANOVA tests (α = 0.05). RESULTS: Significant alterations in the infrared resonances associated with collagen cross-linking within the collagen matrix were observed across all PCP groups. The application of PCP demonstrated a noteworthy enhancement in micro-tensile bond strength (MTBS) compared to group C (p < 0.05). Notably, group C exhibited the lowest MTBS (41 ± 7.7 MPa), whereas group E2 demonstrated the highest MTBS (66 ± 11.9 MPa). Even after undergoing aging, the MTBS of the PCP groups remained superior to that of group C (p < 0.05). The resin tag length in the PCP groups was found to be greater than that of group C, and the occurrence of nanoleakage was comparatively lower in the PCP groups, both before and after aging. Additionally, PCP exhibited a dose-dependent inhibition of matrix metalloproteinases (MMPs) activity, which was statistically significant (p < 0.05). CONCLUSIONS: The utilization of PCP Primer exhibits notable enhancements in bond strength, mitigates nano-leakage, and suppresses enzyme activity within the hybrid layer.

Enhancing dentin bonding through new adhesives formulations with natural polyphenols, tricalcium phosphate and chitosan.

OBJECTIVES: The aim of the study was to develop new adhesive formulations that include natural polyphenols extracted from green tea (GTE), tricalcium phosphate (TCP) and chitosan to improve dentin bonding characteristics and cytotoxicity. METHODS: Four experimental adhesives were formulated under laboratory conditions. The groups differed in the integration of either GTE and/or TCP + chitosan. The four experimental and one clinically proven reference adhesive underwent shear bond testing after 24 h and 6 months of aging (n = 200) with subsequent fractographic analysis. Bond morphology was analyzed under a scanning electron microscope. The presence of phenolic compounds was validated by high performance liquid chromatography. Cytotoxicity was assessed by the WST-1 colorimetric assay on eluates up to 6 months. Statistical analysis was performed by one- and three-way ANOVA, Games-Howell and Tukey's post-hoc test as well as multiple students t-tests (α = 0.05). Weibull analysis was further conducted. RESULTS: The addition of GTE into the bonding agent did show immediate (p = 0.023, p = 0.013) and long-term (p < 0.001) effects on bond strength. After 24 h, GTE doped groups performed equal to the reference (p = 0.501, p = 0.270) and TCP and chitosan displayed improvements in reliability (m=4.0, m=4.3). Bond strength is retained after aging by adding GTE (p = 0.983). The additional presence of TCP and chitosan reduces it (p = 0.026). Excluding cohesive and mixed failures, the reference adhesive performed statistically equal to three of the four experimental groups. No long-term cytotoxic effects were shown. SIGNIFICANCE: The integration of GTE can enhance bond strength and a calcium source helps to improve immediate bond reliability.

Development of a new universal adhesive containing CPNE7-derived peptide and its potential role in reducing postoperative sensitivity.

Post-operative sensitivity (POS) is the most common clinical dental complaint after tooth preparation and resin-based composite restoration. In our previous study, copine 7 (CPNE7) and CPNE7-derived peptide (CPNE7-DP) induced in vitro odontoblast differentiation and in vivo dentin formation. Here, we incorporated CPNE7-DP into All-Bond Universal (ABU) adhesive, developing ABU/CPNE7-DP. This study aimed to investigate the possibility of reducing POS using ABU/CPNE7-DP. We first determined the stability of CPNE7-DP under low pH. Furthermore, we evaluated its dentinal tubule penetration, in vitro odontogenic differentiation potential, in vivo tertiary dentin formation and its effects on bonding performance. CPNE7-DP was stable at pH 1.2, even lower than ABU's pH of 3.2. ABU/CPNE7-DP can penetrate dentinal tubules, stimulate odontoblast differentiation in vitro and generate tertiary dentin with tubular structure in vivo without interfering with bonding performance. Therefore, ABU/CPNE7-DP may serve as a novel bioactive adhesive for reducing POS.

Bond strength comparison among 10-MDP-containing and non-10-MDP-Containing adhesives in different degrees of dental fluorosis / Comparación de fuerza de unión entre adhesivos que contienen y no contienen 10-MDP en diferentes grados de fluorosis dental

Dental fluorosis can cause changes in the enamel surface, conditioning its functionality and esthetics. The application of dental adhesives is a treatment option; however, their use on fluorotic teeth can result in limitations. The aim of this study was to compare the shear bond strength of two different adhesives, one with 10-MDP and one without 10-MDP, in different degrees of dental fluorosis.This is an in vitro study on dental enamel samples, a total of 180 samples with the inclusion criteria were treated, randomly divided into two groups of 90, according to the type of dental adhesive, where each group was again divided into three groups of 30 samples, representing different degrees of dental fluorosis according to the Thylstrup-Fejerskov index (Group I: TF1 and TF2; Group II: TF3; Group III: TF4). Normality tests, two-factor ANOVA, and post-hoc tests were used to determine differences between the groups, with a significance level of 95%. As results, a statistically significant difference was shown between the use of dental adhesive with 10-MDP and the three groups of dental fluorosis (p=0.011), in addition, a Tukey post-hoc test on the groups treated with 10-MDP adhesive revealed a statistically significant difference between group I versus group II, and group I versus group III, (p=<0.05). It is concluded that the use of adhesive systems with 10-MDP presents a better shear bond strength on enamel with dental fluorosis grades I and II in the Thylstrup-Fejerskov index.

La fluorosis dental puede ocasionar cambios en la superficie del esmalte, condicionando su funcionalidad y estética, la aplicación de adhesivos dentales es una opción de tratamiento, sin embargo, su uso en dientes fluoroticos puede resultar en limitaciones. El objetivo de este estudio consistió en comparar la fuerza de adhesión a la cizalladura de dos diferentes adhesivos, uno con 10-MDP y otro sin 10-MDP, en diferentes grados de fluorosis dental. Se trata de un estudio in vitro en muestras de esmalte dental, un total de 180 muestras con los criterios de inclusión fueron tratadas, aleatoriamente divididas en dos grupos de 90, de acuerdo al tipo de adhesivo dental, donde cada grupo fue dividido nuevamente en tres grupos de 30 muestras, representando diferentes grados de fluorosis dental según el índice de Thylstrup- Fejerskov (Grupo I: TF1 y TF2; Grupo II: TF3; Grupo III: TF4). Para determinar diferencias entre los grupos se utilizaron pruebas de normalidad, ANOVA de dos factores, y pruebas post-hoc, con un nivel de significancia de 95%. Como resultados, se mostró una diferencia estadísticamente significativa entre el uso de adhesivo dental con 10- MDP y los tres grupos de fluorosis dental (p=0.011), además, una prueba post hoc de Tukey sobre los grupos tratados con adhesivo 10-MDP revelaron una diferencia estadísticamente significativa entre el grupo I frente al grupo II, y el grupo I frente al grupo III, (p=<0.05) Se concluye que el uso de sistemas adhesivos con 10-MDP presentan una mejor resistencia de adhesión al cizallamiento en esmalte con grados de fluorosis dental I y II en el índice de Thylstrup-Fejerskov

Bond strength of composite resin/universal adhesive to dentin submitted to radiotherapy / Fuerza de unión de resina compuesta/adhesivo universal a dentina sometida a radioterapia

Aim: To evaluate the bond strength of a universal adhesive system to dentin submitted to radiotherapy. Materials and Methods: Sixty extracted human teeth were divided into two groups (n = 30): without radiotherapy (control); with radiotherapy, according to the adhesive protocol (n=15): ER-etch-and-rinse (acid + Single Bond Uni-versal); SE-self-etch (Single Bond Universal). The analyzes were shear bond strength (SBS) (n=10), failure pattern (n=10) and scanning electron microscopy (n=5). Data was analyzed by a two-way ANOVA (α =0.05). Results: The radiotherapy decreased SBS of the restorative material to dentin (p<0.0001). The ER protocol provided lower bond strength values (p<0.001). The predominant type of fracture without radiotherapy was mixed (SE), cohesive to the material (ER). Both protocols presented adhesive failures with radiotherapy. Teeth had a hybrid layer and long resin tags (without radiotherapy) and few tags (with radiotherapy). Conclusions: The SE adhesive mode favors the shear bond strength of resin to dentin in teeth submitted to radiotherapy.

Objetivo: Evaluar la fuerza de adhesión de un sistema adhesivo universal a la dentina sometida a radioterapia. Materiales y Métodos: Sesenta dientes humanos extraídos se dividieron en dos grupos (n = 30): sin radioterapia (control); con radioterapia, según protocolo adhesivo (n=15): ER-grabado y enjuague (ácido + Single Bond Universal); autograbado SE (Single Bond Universal). Los análisis ejecutados fueron resistencia al cizallamiento (SBS) (n=10), patrón de falla (n=10) y microscopía electrónica de barrido (n=5). Los datos se sometieron al test de ANOVA de dos vías (α =0,05). Resultados: La radioterapia disminuyó la SBS del material restaurador a la dentina (p<0,0001). El protocolo ER proporcionó valores de fuerza de unión más bajos (p<0,001). El tipo de fractura predominante sin radioterapia fue mixta (SE), cohesiva al material (ER). Ambos protocolos presentaron fallas adhesivas con radioterapia. Los dientes tenían una capa híbrida y colas de resina largas (sin radioterapia) o pocas colas de resina (con radioterapia). Conclusión: El modo adhesivo SE favorece la resistencia al corte de la resina a la dentina en dientes sometidos a radioterapia.

Effect of a cross-linking antioxidant agent on the bond strength of adhesive resin to irradiated dentin.

It has been shown that irradiation can cause structural changes in dentin that may reduce the bond strength of adhesives to dentin. Applying cross-linking or antioxidant agents may help reverse this detrimental effect and improve adhesion to dentin. This in vitro study aimed to evaluate the effects of epigallocatechin-3-gallate (EGCG) pretreatment and the time of adhesive bonding (24 hours vs 1 month) on the shear bond strength (SBS) of All-Bond Universal (ABU) to irradiated dentin using etch-and-rinse (ER) and self-etching (SE) modes. Flat dentin surfaces prepared from 96 extracted intact human molars were divided into 8 groups (n = 12) and bonded with ABU. In the control (CO) groups (CO/ER and CO/SE), bonding was performed on nonirradiated dentin; in the irradiated (IR) groups (IR/ER and IR/SE), bonding was performed on irradiated dentin; in the irradiated pretreated groups (IR/EGCG/ER and IR/EGCG/SE), irradiated dentin received a 0.1% EGCG pretreatment before bonding; and in the irradiated delayed bonding (DL) groups (IR/DL/ER and IR/DL/SE), bonding on irradiated dentin was performed 1 month after completion of radiotherapy. The irradiation protocol consisted of a total dose of 60 Gy with 2-Gy exposure applied 5 days per week for a period of 6 weeks. After bonding procedures were completed, the specimens were stored in 100% humidity at 37°C for 24 hours and then the SBS was tested in a universal testing machine. Data were analyzed using 1-way analysis of variance and Tukey tests. There was a statistically significant difference among the 8 groups (P < 0.001). Irradiation diminished the SBS in the IR/ER and IR/SE groups compared with their controls (P < 0.001). Pretreatment with EGCG significantly increased the SBS in the IR/EGCG/ER group only (P < 0.001). The difference between the IR/ER and IR/DL/ER groups was not statistically significant, and the difference between the IR/SE and IR/DL/SE groups was marginally significant (P = 0.056). Pretreatment with EGCG after acid etching restored the SBS of ABU to irradiated dentin, resulting in an adhesive performance equivalent to that observed with nonirradiated dentin. A 1-month delay between irradiation and bonding did not improve the SBS.

Efecto de diferentes condiciones y modos de aplicación sobre la fuerza de unión de los adhesivos a la dentinaEffect of different conditions and modes of application on bond strength of adhesives to dentine / Effect of different conditions and modes of application on bond strength of adhesives to dentine

Objective: To evaluate the microtensile bond strength in different dentine conditions (etched-E, non-etched-N, dry-D and wet-W) of a multimode adhesive (Scotchbond Universal-SU, 3M/ESPE) and a total etching adhesive (Ambar-AB, FGM) using a sonic device (Smart Sonic Device-SD, FGM). Material and methods: In this in vitro study, ninety six sound extracted human molars were divided into 12 groups (n=8) according to different dentine conditions and adhesive systems. Enamel was removed and the middle dentine surfaces were polished. Each adhesive system was applied according to the different dentine conditions, and composite resin blocks were incrementally built up and stored for 24 hours. Specimens were sectioned into sticks and bond strength data were analyzed with the Kruskal-Wallis test and Mann-Whitney U tests. Results: No effects of sonic application and were observed. In general, AB showed lower results compared to the SU. E and N conditions did not statistically affect the bond strength of SU groups. Dry dentine presented statistically superior bond strength values when compared to wet dentine for SU/E/SD group. Conclusion: Adhesion of dry dentine with multimode adhesive system may be superior to wet dentine with sonic application. The modes of application had no influence in bond strength of studied adhesives.

Objetivo: Evaluar la resistencia de la unión microtensil en diferentes condiciones de dentina (grabado-E, sin grabado-N, seco-D y húmedo-W) de un adhesivo multimodo (Scotchbond Universal-SU, 3M/ESPE) y un adhesivo de grabado total (Ambar-AB, FGM) utilizando un dispositivo sónico (Smart Sonic Device-SD, FGM). Material y Métodos: En este estudio in vitro, noventa y seis molares humanos extraídos sanos se dividieron en 12 grupos (n=8) de acuerdo con diferentes condiciones de dentina y sistemas adhesivos. Se eliminó el esmalte y se pulieron las superficies centrales de la dentina. Cada sistema adhesivo se aplicó de acuerdo con las diferentes condiciones de dentina, y los bloques de resina compuesta se acumularon de forma incremental y se almacenaron durante 24h. Las muestras se seccionaron en barras y los datos de resistencia de la unión se analizaron con la prueba de Kruskal-Wallis y la prueba de U de Mann-Whitney. Resultado: No se observaron efectos de la aplicación sónica. En general, AB mostró resultados más bajos en comparación con el SU. Las condiciones E y N no afectaron estadísticamente la fuerza de unión de los grupos SU. La dentina seca presentó valores de fuerza de adhesión estadísticamente superiores en comparación con la dentina húmeda para el grupo SU/E/SD. Conclusión: La adhesión de la dentina seca con un sistema adhesivo multimodo puede ser superior a la dentina húmeda con aplicación sónica. Los modos de aplicación no tuvieron influencia en la resistencia de la unión de los adhesivos estudiados.

Inducing cathepsin L expression/production, lysosomal activation, and autophagy of human dental pulp cells by dentin bonding agents, camphorquinone and BisGMA and the related mechanisms.

Camphorquinone (CQ) and resin monomers are included in dentin bonding agents (DBAs) and composite resin to restore tooth defects due to abrasion, crown fracture, or dental caries. DBAs, CQ, and bisphenol A-glycidyl methacrylate (BisGMA) applications influence the biological activities of the dental pulp. The current investigation aimed to delineate the effect of DBAs, CQ, and BisGMA on cathepsin L production/expression, lysosomal activity, and autophagy induction in human dental pulp cells (HDPCs). HDPCs were exposed to DBAs, CQ, or BisGMA with/without inhibitors for 24 h. Enzyme-linked immunosorbent assay was employed to determine the cathepsin L level in culture medium. The cell layer was utilized to measure cell viability by 3-(4,5-dimethyl-thiazol-2-yl)-2,5-diphenyl -tetrazolium bromide (MTT) assay. Real-time PCR was used to evaluate the mRNA expression. Western blotting or immunofluorescent staining was used to study protein expression. Lysosomal density was evaluated by lysotracker red staining. We found that DBAs, CQ, and BisGMA stimulated cathepsin L mRNA, protein expression, and production in HDPCs. In addition, CQ and BisGMA induced lysosomal activity, Beclin1, ATG12, LC3B, Bax, and p53 expression in HDPCs, indicating the stimulation of autophagy. Glutathione (GSH) prevented CQ- and BisGMA-induced cytotoxicity. Moreover, E64d, cathepsin L inhibitor (two cathepsin inhibitors), and Pifithrin-α (a p53 inhibitor) showed little preventive effect toward CQ- and BisGMA-induced cytotoxicity. Autophagy inhibitors (NH4Cl, Lys05) mildly enhanced the CQ- and BisGMA-induced cytotoxicity. These results indicate that DBAs stimulated cathepsin L, possibly due to their content of CQ and BisGMA that may induce cathepsin L in HDPCs. CQ and BisGMA stimulated lysosomal activity, autophagy, and apoptosis, possibly via induction of Beclin 1, ATG12, LC-3B, Bax, and p53 expression. In addition, CQ and BisGMA cytotoxicity was related to redox change and autophagy. These events are important role in pulpal changes after the restoration of tooth decay using CQ- and BisGMA-containing DBAs and resin composite.

Dentin permeability after pretreatment with titanium tetrafluoride and self-etching or universal adhesive systems

Aim: To evaluate dentin permeability after pretreatment with 2.5% aqueous solution of titanium tetrafluoride (TiF4), followed by a self-etching universal adhesive system. Methods: Forty dentin discs (1.5 mm thick) were randomly divided into groups according to the application or non-application of a pretreatment, and the type of adhesive system to be tested (two-step self-etching/ Clearfil SE Bond/ Kuraray Medical, or universal adhesive system/ Single Bond Universal/ 3M ESPE). Both sides of the discs were conditioned with 37% phosphoric acid to remove the smear layer. The first hydraulic conductivity measurement (L1) was performed in a permeability machine, under 5 PSI pressure. The samples were sanded again to form a standardized smear layer. The teeth designated for pre-treatment with TiF4 received the TiF4 solutions applied actively for 60 seconds, and the adhesive systems were applied according to the manufacturer's instructions. Then, a new hydraulic conductivity measurement (L2) was performed for the purpose of calculating the hydraulic conductance at a later time, considering the water viscosity and the thickness of the specimen. The percentage (L) of dentin permeability after application of the adhesive system was obtained (L (%) = [(L1-L2) x100] / L1). The Mann-Whitney non-parametric test was applied. Results: There was no difference between the two adhesive systems, or between the groups with or without pretreatment, as regards dentin permeability (p>0.05). Conclusion: Pretreatment with 2.5% TiF4 did not influence dentin permeability, irrespective of the adhesive system used

Impact of photoinitiator quality on chemical-mechanical properties of dental adhesives under different light intensities / Impacto da qualidade de fotoiniciadores nas propriedades químico mecânicas de adesivos dentais sob diferentes intensidades de luz

Objective: Evaluate the mechanical properties of experimental adhesive models with different photoinitiators (PI) polymerized by LED units of different power densities. Material and Methods: Three groups of adhesive models based on HEMA/BisGMA (45/55) were prepared in association with different PI combinations: G2 (control) ­ 2 PI: 0.5% CQ, 0.5% EDMAB; G3 - 3 PI: 0.5% CQ; 0.5% DMAEMA, 0.5% DPIHP; G4 - 4 PI: 0.5% CQ; 0.5% EDMAB; 0.5% DMAEMA; 0.5% DPIHP. The three formulations were polymerized at two different LED power densities: 550 mW/cm2 and 1200 mW/cm2. The degree of conversion (DC) of adhesive monomers was monitored in situ through the FTIR for 600 s. Specimens were prepared for each formulation for analysis mong adhesive systems (G2

Objetivo: Avaliar as propriedades mecânicas de modelos adesivos experimentais com diferentes fotoiniciadores (PI) polimerizados por unidades de LED de diferentes densidades de energia. Material e Métodos: Três grupos de modelos adesivos baseados em HEMA/BisGMA (45/55) foram preparados em associação com diferentes combinações de PI: G2 (controle) ­ 2 PI: 0,5% CQ, 0,5% EDMAB; G3 - 3PI: 0,5% CQ; 0,5% DMAEMA, 0,5% DPIHP; G4 - 4 PI: 0,5% CQ; 0,5% EDMAB; 0,5% DMAEMA; 0,5% DPIHP. As três formulações foram polimerizadas em duas densidades de potência de LED: 550 mW/cm2 e 1200 mW/cm2. O grau de conversão (DC) dos monômeros adesivos foi monitorado in situ através do FTIR durante 600 s. Amostras foram preparadas para cada formulação para análise de resistência à flexão (FS), módulo de elasticidade (ME), sorção (SOR) e solubilidade (SOL). Os dados foram submetidos aos testes ANOVA 2-fatores e Tukey (5%). Resultados: DC: houve diferença significativa entre os sistemas adesivos (G2

Effect of time and dental substrate on the bond strength of a universal adhesive system: in vitro study / Efeito do tempo e do substrato dental na resistência de união de um sistema adesivo universal: estudo in vitro

Introduction: Dentin adhesives provide union between the dental substrate and composite resin, but this union can be influenced by the cleaning agent. Objective: Evaluate the use of ozonated water as a cavity cleaning solution. Material and method: 40 bovine dental crowns were selected, divided into four groups: AD (dentin cleaning with distilled water) and AO (dentin cleaning with ozonized distilled water). Each group was divided into two storage periods (24h and 30 days) kept at 37 °C. The selected universal system adhesive was employed according to the manufacturer's instructions and light cured for 20 seconds. At that time, three cylinders were made (Tygon matrix with an internal diameter of 2 mm and a height of 2 mm) of composite resin in the crowns in the cervical, médium, and incisal regions and light cured for 30 seconds. After storage, the bonding strength was tested by micro-shear, and fracture type analysis was performed. The data were submitted to statistical analysis using the Shapiro-Wilk test with a significance level of 95%, ANOVA, and Turkey. Result: There was a statistically significant difference between the bond strength values, only in the intergroup analysis for the time of 24 hours, between the middle third of the groups (LDAO24 = 2.70 (± 2.39); LDAO30 = 3.82 (± 2.31)). The predominant fracture type for both groups was an adhesive fracture, except in the medium and incisal thirds of the AD, which was a cohesive dentin fracture. Conclusion: The utilization of ozone did not change the bond strength adhesive.

Introdução: Os adesivos dentinários proporcionam união entre o substrato dental e resina composta, porém esta união pode ser influenciada pelo agente de limpeza. Objetivo: Avaliar a influência na resistência de união (RU) de um sistema adesivo universal associado à da água ozonizada como solução de limpeza cavitária. Material e método: Foram selecionadas 40 coroas de dentes anteriores bovinos divididos em 4 grupos: AD (limpeza dentinária com água destilada) e AO (limpeza dentinária com água destilada ozonizada). Cada grupo foi subdividido em outros dois grupos de acordo com o tempo de armazenamento (24h e 30 dias) armazenados a 37ºC. A limpeza dentinária foi realizada por meio de uma seringa de 60mL de cada solução e fricção por 10 segundos. O sistema adesivo universal selecionado foi aplicado de acordo com as instruções do fabricante e fotoativado por 20 segundos. Em seguida, foram confeccionados 3 cilindros (matriz Tygon com um diâmetro interno de 2 mm e 2 mm de altura) de resina composta nas coroas nas regiões cervical, média e incisal e fotoativados por 30 segundos. Após o armazenamento foi realizado o teste de RU por microcisalhamento e análise do tipo de fratura. Os dados coletados foram submetidos a análise estatística através do teste de Shapiro Wilk com nível de significância de 95%, ANOVA e Tukey. Resultado: Houve diferença estatística significativa entre os valores de RU apenas na análise intergrupos para o tempo de 24 horas, entre o terço médio dos grupos (LDAO24 = 2,70 (± 2,39); LDAO30 = 3,82 (± 2,31)). O tipo de fratura predominante para ambos os grupos em todos os tempos foi de fratura adesiva, com exceção ao terço médio e incisal do AD, que foi fratura coesiva de dentina. Conclusão: A utilização do ozônio não alterou a resistência de união adesiva.

Influence of two natural cross-linkers on microtensile bond strength durability ­ An in vitro study / Influência de dois reticuladores naturais na durabilidade da resistência de união à microtração ­ Um estudo in vitro

Objective: to investigate the effect of two natural cross-linkers on microtensile bond strength (µTBS) and evaluate their influence on the durability of the resin dentin bonds. Material and Methods: the Moringa oleifera and Centella asiatica plant extracts were qualitatively tested with high-performance thin layer chromatography (HPTLC) for the presence of phenols. The phenolic content ranged from 27 to 30 gallic acid equivalents (GAE), µg/mg of dry weight. After etching, two concentrations (5% and 1%) of these two extracts were prepared and used as pretreatment liners on dentin. They were applied for a min. After restoration with resin composite, dentin resin beams were prepared. The study groups were 5% Moringa, 1% Moringa 5% Centella 1% Centella, and control (without cross-linker application). For each group, half of the samples underwent µTBS testing after 24 hours, while the remaining half were immersed in artificial saliva to assess the bond's longevity after 6 months of ageing. Statistical analysis was performed using one-way ANOVA followed by Tukey's post hoc test. Results: both 5% and 1% Moringa showed a significant difference (p<0.05) compared to the other groups at both intervals. However, after ageing, the specimens in the control and 1% Centella groups resulted in a significant decrease in µTBS. Conclusion: overall, both concentrations of Moringa (5% and 1%) were effective in stabilising the bond during both intervals.(AU)

Objetivo: investigar o efeito de dois reticuladores naturais na resistência de união (µTBS) à microtração e avaliar sua influência na durabilidade da adesão da resina à dentina. Material e Métodos: extratos das plantas Moringa oleifera e Centella asiatica foram qualitativamente testados através de cromatografia em camada fina de alta performance (HPTLC) para a presença de fenóis. O conteúdo fenólico alcançou entre 27 a 30 equivalentes de ácido gálico (GAE), µg/mg de peso seco. Após o condicionamento, duas concentrações (5% e 1%) dos extratos foram preparadas e utilizadas como forros de pré-tratamento em dentina. Eles foram aplicados por um minuto. Após a restauração com resina composta, palitos de dentina e resina foram preparados. Os grupos foram 5% Moringa, 1% Moringa, 5% Centella, 1% Centella e controle (sem aplicação de reticulador). Para cada grupo, metade das amostras foram submetidas ao teste µTBS após 24 horas, enquanto a outra metade foi imersa em saliva artificial para avaliar a longevidade adesiva após 6 meses de envelhecimento. Foi realizada análise estatística através de ANOVA 1-fator, seguido do teste post hoc de Tukey. Resultados: ambas as concentrações de 5% e 1% de Moringa demonstraram diferença significativa (p<0.05) comparadas aos outros grupos em ambos os intervalos. No entanto, após o envelhecimento, os espécimes dos geupos controle e 1% de Centella resultaram em uma redução significativa de µTBS. Conclusão: no geral, ambas as concentrações de Moringa (5% e 1%) foram efetivas em estabelecer a adesão em ambos os intervalos (AU)

Effect of adhesive primer application on shear bond strength of self-adhesive cement to tooth structure and two different CAD/CAM milled blocks / Efeito da aplicação do primer adesivo na resistência ao cisalhamento do cimento autoadesivo à estrutura dentária e a dois diferentes blocos fresados CAD/CAM

Objective: This study was conducted to evaluate the influence of the G-CEM ONE adhesive enhancing primer on the shear bond strength of self-adhesive resin cement (G-CEM ONE) to both tooth structure and two different CAD/CAM blocks (GC Initial LiSi and Cerasmart 270). Material and Methods: Forty specimens (cylindrical-shaped, 5 mm in diameter and height) were milled from both CAD/CAM blocks (20 specimens from each block type). Forty sound upper premolars were sectioned to the level of peripheral dentin, then randomly divided into four groups (n = 10): A1: GC Initial LiSi without adhesive enhancing primer; B1: Cerasmart 270 without adhesive enhancing primer; A2: GC Initial LiSi with adhesive enhancing primer; B2: Cerasmart 270 group with adhesive enhancing primer application. The CAD/CAM blocks were cemented on teeth using a self-adhesive resin cement (G-cem one). The shear bond strength was assessed using a computerized universal testing machine. A digital microscope was used to study the mode of failure. The shear bond strength values data were analyzed statistically using paired t-test and independent t-test at the significance level of (0.05). Results: A significant difference was shown in the shear bond strength values among groups (P =0.000). The highest shear bond strength value was revealed in group A2, while group B1 exhibited the lowest shear bond strength value. Conclusion: Using the adhesive enhancing primer on the tooth's surface improved the resin cement's bond strength to CAD/CAM blocks. Additionally, GC Initial LiSi exhibited higher bond strength than Cerasmart 270, with or without the primer (AU)

Objetivo: Este estudo foi conduzido para avaliar a influência do primer adesivo G-CEM ONE na resistência ao cisalhamento do cimento resinoso autoadesivo (G-CEM ONE) tanto na estrutura dentária quanto em dois diferentes blocos CAD/CAM (GC Initial LiSi e Cerasmart 270). Material e Métodos: Quarenta corpos de prova (formato cilíndrico, 5 mm de diâmetro e altura) foram fresados em blocos CAD/CAM (20 corpos de prova de cada tipo de bloco). Quarenta pré-molares superiores sadios foram seccionados até o nível da dentina mais externa e, em seguida, divididos aleatoriamente em quatro grupos (n = 10): A1: GC Initial LiSi sem primer adesivo; B1: Cerasmart 270 sem primer adesivo; A2: GC Initial LiSi com primer adesivo; B2: Grupo Cerasmart 270 com aplicação de primer adesivo. Os blocos CAD/CAM foram cimentados nos dentes com cimento resinoso autoadesivo (G-CEM ONE). A resistência ao cisalhamento foi avaliada utilizando uma máquina de ensaios universal computadorizada. Um microscópio digital foi utilizado para estudar o modo de falha. Os dados dos valores de resistência ao cisalhamento foram analisados estatisticamente por meio do teste t pareado e teste t independente ao nível de significância de (0,05). Resultados: Foi demonstrada diferença significativa nos valores de resistência ao cisalhamento entre os grupos (P =0,000). O maior valor de resistência ao cisalhamento foi revelado no grupo A2, enquanto o grupo B1 exibiu o menor valor de resistência ao cisalhamento. Conclusão:A utilização do primer adesivo na superfície dentária melhorou a resistência de união do cimento resinoso aos blocos CAD/CAM. Além disso, o GC Initial LiSi apresentou maior resistência de união que o Cerasmart 270, com ou sem primer.(AU)

Acid-Base Resistant Zone in Teeth with the Direct Restoration Using Different Adhesive System Generations: A Systematic Review

ABSTRACT Objective: To find out what the acid-base resistant zone (ABRZ) is and the mechanism of its formation. Material and Methods: This systematic review was based on the search of laboratory studies in which selfetching adhesive systems were used. The electronic database PubMed was used for the search. The search began on August 2021 and ended on June 2022. We have analyzed the materials and methods of each research and entered them in the appropriate tables to give a clearer assessment of the obtained results. Results: This systematic review included 15 full-text articles published from 2011 to 2019. The ABRZ is formed on both dentine and enamel. On dentine, the ABRZ is formed only when using self-etching adhesive systems; on the enamel, on the contrary, the step of preliminary etch and rinse contributes to the formation of a thicker ABRZ. The functional monomer MDP and fluorine increase the thickness of the ABRZ and provide a hybrid layer /ABRZ boundary without defects and erosions. Conclusion: Self-etching adhesive systems ensure the creation of an ABRZ resistant to acid-base tests. This phenomenon can provide the resistance of tooth tissues to demineralization, and therefore increase their resistance to caries.

Mineral Density Distribution Differences in Enamel and Dentin Tissues in the Teeth Array According to the HU Scale

ABSTRACT Objective: To evaluate the mineral density of enamel and dentin tissues of healthy individuals using threedimensional cone-beam computed tomography. Material and Methods: CBCT images of 15 healthy individuals, previously obtained for various reasons, were used in this study. In HU measurements, mineral density measurements were made from three different regions of enamel and three different regions of dentin, and the values obtained were compared. Enamel and dentin mineralization density measurements were measured from six regions, namely the crown cutting edge, buccal middle and cervical region for enamel, and the crown cutting edge, cervical region and root apex for dentin. In the comparisons of groups, the parametric One-Way ANOVA variance analysis method was applied. In the paired comparisons between the groups, the Tukey HSD test was applied as the multiple comparison post hoc test. A value of p<0.05 was accepted as statistically significant. Results: Mineralization density of tooth enamel and dentin tissues was quantitatively different in the maxilla and mandible in anterior and posterior teeth. Conclusion: In all the teeth, there were statistically significant decreases in the mineral density values of enamel and dentin tissue from occlusal towards the cemento-enamel junction. Statistically significant decreases were observed in the mineral density values of enamel and dentin tissue from the anterior region towards the posterior region in the teeth in both the upper and lower jaws.

Influence of chlorhexidine 2% and sodium hypochlorite 5. 25% on micro-tensile bond strength of Universal adhesive system (G-Premio Bond)

Aim One of the reasons for the failure of adhesion in composite restorations and secondary caries may be the chemical irrigants used during the endodontic treatment. NaOCl is widely used for the biomechanical preparation of root canals due to its antimicrobial properties and capacity to dissolve organic material. In addition, another very effective decontamination solution is chlorhexidine 2%. There are few studies about the effect of root canal irrigation solutions on bond strength of universal adhesives therefore, in this study we have investigated the influence of CHX 2% and NaOCl 5.25% on micro-tensile bond strength of G-Premio Bond. Methods Twenty-four human teeth were randomly allocated to the following groups: G1, immersion in saline solution 0.9% for 30 minutes (control); G2, immersion in CHX 2% for 30 minutes; G3, immersion in NaOCl 5.25% for 30 minutes. After restoration, the dentin/resin interface was tested by micro-tensile bond strength. The surfaces morphology was analyzed by Scanning Electron Microscopy. Data were analyzed by ANOVA followed by Tukey test in SPSS software Version 24. Results There was a statistically significant difference between G3 and G1 (P < 0.05). There were no statistically significant differences among G1 and G2, G2 and G3. Conclusion Root canal irrigation with NaOCl 5.25% significantly reduced the micro-tensile bond strength in the G-Premio Bond at self-etch mode, but the use of CHX did not make a significant difference.

Dual-cured adhesive system improves adhesive properties of dentin cavities restored with a bulk-fill resin composite

Aim: To evaluate the impact of a dual-cured adhesive system on the in situ degree of conversion (DC), bond strength (BS) and failure mode (FM) of adhesive interfaces in dentin cavities restored with a bulk-fill resin composite. Methods: 4-mm-deep dentin cavities with a 3.1 C-factor were created in 68 bovine incisors (n = 17 per group). The lightcured (Scotchbond™ Universal) or the dual-cured (Adper™ Scotchbond™ Multi-purpose Plus) adhesive system was applied to the cavities, which were then restored with a bulkfill resin composite (Filtek™ Bulk Fill). In situ DC analysis was performed by means of micro Raman spectroscopy at the top and bottom interfaces. Push-out BS was measured in a universal testing machine after 24-h or 6-month water storage. FM was determined with a stereomicroscope. Data of in situ DC and BS were analyzed by two-way analysis of variance (ANOVA) and Tukey test (p<0.05), while the FM was analyzed descriptively. Results: The groups that received the dual-cured adhesive system showed statistically higher in situ DC and BS than those that received the light-cured adhesive system. Cohesive failure mode was the most frequent in all conditions. Conclusion: In situ DC and BS were influenced by the curing strategies of the adhesive systems with better performance of the dual-cured material

Influence of etching Mode and composite type on bond strength to biodentine using a ''No-Wait'' universal adhesive / Influencia del modo de grabado y del tipo de resina en la resistencia adhesiva al Biodentine utilizando un adhesivo universal tipo "no-wait"

Abstract: The purpose of this study was to compare the shear bond strength (SBS) of four resin-based composite materials to a silicate-based cement using a ''no-wait'' universal bond with self-etch (SE) and etch-and-rinse (ER) modes. Acrylic blocks (n=80, 2mm depth, 5mm diameter central hole) were prepared. The holes were filled with BiodentineTM (BD) and divided into 4 main groups (n=20) according to the composite resin type used: Group FZ250: FiltekTM Z250 Universal Restorative (microhybrid), Group SDR: SDR Plus U Bulk Fill Flowable (low-viscosity bulk-fill), Group FBP: FiltekTM Bulk Fill Posterior (high-viscosity bulk-fill), Group EF: EsFlow™ Universal Flowable Composite (nanohybrid). A 'no-wait' universal bond (Clearfil Universal Bond Quick) was used for bonding application. Then each group was divided into 2 subgroups according to the etching mode applied (ER and SE). SBSs were measured and stereomicroscope was used to identify the failure modes. Selected samples of fracture surfaces were imaged by SEM. Tukey's post-hoc and One-way ANOVA tests were used to analyze data. There were statistically significant differences among the composite groups (p 0.05). The SBS of BD to the resin composites depends on the composite type but application of the 'no-wait' universal bond in different etching modes is regardless of the SBS of BD to resin composites.

Resumen El objetivo de este estudio fue comparar la resistencia de adhesión al cizallamiento (SBS) de cuatro resinas con un cemento a base de silicato utilizando una adhesivo universal "no-wait" de autograbado (SE) y grabado y lavado (ER). Se prepararon bloques acrílicos (n=80, de 2mm de profundidad y un agujero central de 5mm de diámetro). Los agujeros se rellenaron con BiodentineTM (BD) y se dividieron en 4 grupos principales (n=20) según el tipo de resina compuesta utilizada: Grupo FZ250: FiltekTM Z250 Universal Restorative (microhíbrido), Grupo SDR: SDR Plus U Bulk Fill Flowable (bulk-fill de baja viscosidad), Grupo FBP: FiltekTM Bulk Fill Posterior (bulk-fill de alta viscosidad), Grupo EF: EsFlow™ Universal Flowable Composite (nanohíbrido). Para la aplicación de la adhesión se utilizó un adhesivo universal "no-wait" (Clearfil Universal Bond Quick). A continuación, cada grupo se dividió en 2 subgrupos según el modo de grabado aplicado (ER y SE). Se midieron los SBS y se utilizó el estereomicroscopio para identificar los modos de fallo. Las muestras seleccionadas de las superficies de fractura se analizaron mediante SEM. Se utilizaron las pruebas post-hoc de Tukey y ANOVA de una vía para analizar los datos. Hubo diferencias estadísticamente significativas entre los grupos de composites (p0,05). La SBS de la BD a los composites de resina depende del tipo de composite, pero la aplicación de la unión universal "no-wait" en los diferentes modos de grabado es independiente de la SBS de la BD a los composites de resina.